粘贴挤塑板外保温施工工艺
作者:admin 来源:本站 发布时间:2018-02-21 14:32:50 浏览次数:396
1、挤塑板涂刷界面砂浆的配制
1. Preparation of the mortar for the interface of the extrusion plate
济南挤塑板厂家的挤塑板涂刷界面剂:50kg/桶 塑料桶包装,以用滚子或刷子方便滚刷为宜。

Ji'nan plastic plate manufacturer's extruded plate brush interface agent: 50kg/ barrel plastic barrel packaging, in order to use roller or brush to facilitate the roll brush.

济南挤塑板厂家

2、挤塑板粘结砂浆的配制
2. Preparation of extruded board bonded mortar
聚合物砂浆和水按100:22~25 kg重量比用砂浆搅拌机或手提搅拌器搅拌均匀。配制挤塑板粘结砂浆加料次序,应先加入聚合物砂浆,后再加入水继续搅拌3min倒出。挤塑板粘结砂浆不得任意加水,应在2h内用完。
Polymer mortar and water are evenly stirred with a mortar mixer or a portable agitator according to the weight ratio of 100:22 to 25 kg. In addition, the polymer mortar should be added first, then water is added to the mortar to continue to stir 3min. The adhesive mortar of the extruded board shall not be added at any water. It shall be used in 2H.
3、抗裂水泥砂浆的配制
3. Preparation of anti cracking cement mortar
聚合物抗裂砂浆:水按100:22~25 kg重量比用砂浆搅拌机或手提搅拌器搅拌均匀。配制抗裂砂浆加料次序,应先加入聚合物抗裂砂浆,然后再加入水继续搅拌3min倒出。抗裂砂浆不得任意加水,应在2h内用完。
Polymer anti cracking mortar: water is evenly stirred with a mortar mixer or a portable agitator according to the weight of 100:22 to 25 kg. In order to prepare the anti cracking mortar feeding order, the polymer anti cracking mortar should be added first, then water is added to continue to stir 3min and pour out. The anti cracking mortar shall not be added at any water. It should be used in 2H.
我们会用优良的、贴切的服务,让顾客感受到亲情般的温暖,始终视顾客的安全如己如亲。我们会用自然优势打造产品的独特之处,从而给消费者带来享用产品时独特的心境。
We will use a good, appropriate service, let customers feel the warmth of family like, always look at the safety of customers as if they are friendly. We will use the natural advantage to create the unique features of the product, so as to give consumers the unique mood to enjoy the product.
友情链接:幸运彩票官网  博九彩票  幸运彩票官网  博九彩票官网  传奇彩票官网  博九_博九官网  

免责声明: 本站资料及图片来源互联网文章,本网不承担任何由内容信息所引起的争议和法律责任。所有作品版权归原创作者所有,与本站立场无关,如用户分享不慎侵犯了您的权益,请联系我们告知,我们将做删除处理!